High strength silica/natural rubber wet master rubber

HR-M100B wet master rubber is a high-end nano rubber composite material for rubber products and tires and other industries.

Model:

HR-M100B

Classification:

High strength silica/natural rubber wet master HR-M100B

Key words:

High strength silica/natural rubber wet master rubber

　　Product Introduction

HR-M100B wet master rubber is a high-grade nano-rubber composite material for rubber products and tires and other industries. This product is a pre-dispersed rubber matrix material made of a proper amount of modified white carbon black and natural latex by wet premixing. The ash content can be adjusted between 25% and 31%, and it is white or light yellow rubber particles or rubber blocks at room temperature.

　　Product characteristics

Compared with the traditional natural rubber compound, the main advantages of HR-M100B wet master rubber are: silica is evenly dispersed in the rubber matrix, high filling amount, low filler loss rate and high storage stability, which can significantly improve the comprehensive performance of rubber (especially high tensile, high tear and high elongation at break).

　　Application Scenarios

Products are mainly used in truck tires, truck tires, off-highway tires, large engineering vehicle tires and other fields.

　　Packaging and storage

The HR-M100B master glue of the product is packaged in two layers (the inner bag is made of PE film with melting point less than 115 ℃, and the outer bag is sealed woven bag) or vacuum compressed with PE film. The net weight of the product is 20±0.1 kg/bag. If you have other special requirements for product packaging, please contact us. Handling procedure: light loading and light unloading, to prevent damage. Storage requirements: Store in dry area. It should be stored separately from easily (combustible) materials and acids, and mixed storage is not allowed. Avoid direct sunlight, waterproof and moisture-proof. If this substance is placed in a flammable solvent, use a suitable ground to avoid an electrical fire. Surface modification of the product caused by calcination or mixing with other additives may alter the toxicological properties. Therefore, we recommend that the product be used within 12 months of production.

Table 1High-strength type IISilica/natural rubber wet mixing master rubberHR-M100B technical indicators

(Suggestion: curing temperature and time 150 ℃,15min or T₉₀ 5min）

Serial Number	Project	Unit	HR-M100B	Inspection method
1	Appearance	/	visual inspection	White or light yellow glue block
2	300% constant elongation stress	MPa	＞10	GB/T528-2009
3	Tensile strength (150^oC)	MPa	＞27	GB/T528-2009
4	Elongation at break	%	＞500	GB/T528-2009
5	Tear strength (150^oC)	KNm^-1	＞90	GB/T528-2009
6	Shore A hardness (25min)	Degree	65-75	GB/T531.1-2008
7	Volatile (105^oC)	%	≤ 2	GB/T24131-2009
8	Ash (950^oC)	%	26-31	GB/T4498.1-2013
9	Mooney viscosity MS(1 8)120 ℃	N · s/m²	85-110	GB/T 1232.1-2016

None

Related Products

Low rolling resistance silica/natural rubber wet master rubber

HR-M300B wet master rubber is a high-grade nano-rubber composite material for rubber products and tires and other industries.

Low heat generation silica/natural rubber wet master rubber

HR-M220B and HR-M221B wet master batches are high-grade nano-rubber composites for rubber products and tires.

High strength silica/natural rubber wet master rubber

HR-M100B wet master rubber is a high-end nano rubber composite material for rubber products and tires and other industries.

Full Formula Wet Mixing Rubber for Slurry Pump

This product is made of the right amount of modified white carbon black, natural rubber latex, vulcanizing agent, accelerator, antioxidant and other processing.

Message

We will contact you within one working day. Please pay attention to your email.