Damping Damping Adhesive Full Formula Wet Mixing HR-Q600B

Key words:

Damping Damping Adhesive Full Formula Wet Mixing Adhesive

　Product Introduction

HR-Q600B full-formula wet compound is a high-grade nano-rubber composite material dedicated to the field of rubber shock-absorbing products. This product is made of the right amount of carbon black, modified white carbon black, natural latex, vulcanizing agent, accelerator, antioxidant and other processing aids by wet mixing of the full formula compound, room temperature for black film.

Product characteristics

Compared with the traditional natural rubber compound, the main advantages of HR-Q600B full formula wet compound are: energy saving, environmental protection, uniform dispersion of fillers in the rubber matrix, high filling amount, low filler loss rate and high storage stability, which can significantly improve the comprehensive performance of rubber (especially high rebound and low compression heat generation performance).

Application Scenarios

The products are mainly used in the field of rubber products such as engineering rubber shock absorbers, air springs, shock absorbers and automotive rubber shock absorbers, with excellent performance such as high rebound and low heat generation.

　　Packaging and storage

The product HR-Q600B full-formula wet compound is plasticized, shaded, treated with rubber isolation agent, stacked and stored on plastic pallets, sealed with plastic wrap, with a net weight of 1000±0.5kg per pallet. If you have other special requirements for product packaging, please contact us. Handling procedure: light loading and light unloading, to prevent damage. Storage requirements: Store in dry area. It should be stored separately from easily (combustible) materials and acids, and mixed storage is not allowed. Avoid direct sunlight, waterproof and moisture-proof. If this substance is placed in a flammable solvent, use a suitable ground to avoid an electrical fire. Surface modification of the product caused by calcination or mixing with other additives may alter the toxicological properties. Therefore, we recommend that the product be used within 12 months of production.

Table 1Shock absorption damping glue full formula wet mixing glue HR-Q600B technology.Technical indicators

(Suggestion: curing temperature and time 150 ℃,20min)

Serial Number	Project	Unit	HR-Q600B	Inspection method
1	Appearance	/	visual inspection	black grainy
2	300% constant elongation stress	MPa	＞6	GB/T528-2009
3	Tensile strength (150^oC)	MPa	＞20	GB/T528-2009
4	Elongation at break	%	＞500	GB/T528-2009
5	Tear strength (150^oC)	KNm^-1	＞20	GB/T528-2009
6	Shore A hardness (25min)	Degree	40-60	GB/T531.1-2008
7	Vulcanized rubber resilience (20min)		45-70	GB/T1681-2009

None

Related Products

Low rolling resistance silica/natural rubber wet master rubber

HR-M300B wet master rubber is a high-grade nano-rubber composite material for rubber products and tires and other industries.

Low heat generation silica/natural rubber wet master rubber

HR-M220B and HR-M221B wet master batches are high-grade nano-rubber composites for rubber products and tires.

High strength silica/natural rubber wet master rubber

HR-M100B wet master rubber is a high-end nano rubber composite material for rubber products and tires and other industries.

Full Formula Wet Mixing Rubber for Slurry Pump

This product is made of the right amount of modified white carbon black, natural rubber latex, vulcanizing agent, accelerator, antioxidant and other processing.

Message

We will contact you within one working day. Please pay attention to your email.