Full Formula Wet Mixing Rubber for Slurry Pump

This product is made of the right amount of modified white carbon black, natural rubber latex, vulcanizing agent, accelerator, antioxidant and other processing.

Model:

HR-Q500B

Classification:

Full Formula Wet Mixing Rubber HR-Q500B for Slurry Pump

Key words:

Full Formula Wet Mixing Rubber for Slurry Pump

　Product Introduction

HR-Q500B full-formula wet compound is a high-grade nano-rubber composite material dedicated to the field of slurry pump. This product is made of the right amount of modified white carbon black, natural rubber latex, vulcanizing agent, accelerator, antioxidant and other processing aids by wet mixing of the whole formula wet mixing rubber, room temperature for dark green film.

　Product characteristics

Compared with the traditional natural rubber compound, the main advantages of HR-Q500B full-formula wet compound are: energy saving and consumption reduction, green environmental protection, uniform dispersion of white carbon black in the rubber matrix, high filling amount, low filler loss rate and high storage stability, which can significantly improve the comprehensive performance of rubber (especially high tensile, high tear, high rebound and high resistance).

　Application Scenarios

Products are mainly used in mining, mining, construction and industrial applications in the slurry pump lining rubber sheet, with high rebound, impact resistance, high tear resistance and other excellent performance.

　　Packaging and storage

The product HR-Q500B full-formula wet compound is plasticized, sheeted, treated with rubber isolation agent, stacked and stored on plastic pallets, sealed with plastic wrap, with a net weight of 1000±0.5kg per pallet. If you have other special requirements for product packaging, please contact us. Handling procedure: light loading and light unloading, to prevent damage. Storage requirements: Store in dry area. It should be stored separately from easily (combustible) materials and acids, and mixed storage is not allowed. Avoid direct sunlight, waterproof and moisture-proof. If this substance is placed in a flammable solvent, use a suitable ground to avoid an electrical fire. Surface modification of the product caused by calcination or mixing with other additives may alter the toxicological properties. Therefore, we recommend that the product be used within 12 months of production.

Table 1HR-Q500B Technology of Full Formula Wet Mixing Rubber for Slurry PumpTechnical indicators

(Suggestion: performance test vulcanization temperature and time 130 ℃,30min or 50min)

Serial Number	Project	Unit	HR-Q500B	Inspection method
1	Appearance	/	visual inspection	Dark green flake solid
2	300% constant elongation stress	MPa	＞7	GB/T528-2009
3	Tensile strength (130^oC)	MPa	＞29	GB/T528-2009
4	Elongation at break	%	＞550	GB/T528-2009
5	Tear strength (130^oC)	KNm^-1	＞90	GB/T528-2009
6	Shore A hardness (25min)	Degree	50-70	GB/T531.1-2008
7	Vulcanized rubber resilience (20min)		45-65	GB/T1681-2009

None

Related Products

Low rolling resistance silica/natural rubber wet master rubber

HR-M300B wet master rubber is a high-grade nano-rubber composite material for rubber products and tires and other industries.

Low heat generation silica/natural rubber wet master rubber

HR-M220B and HR-M221B wet master batches are high-grade nano-rubber composites for rubber products and tires.

High strength silica/natural rubber wet master rubber

HR-M100B wet master rubber is a high-end nano rubber composite material for rubber products and tires and other industries.

Full Formula Wet Mixing Rubber for Slurry Pump

This product is made of the right amount of modified white carbon black, natural rubber latex, vulcanizing agent, accelerator, antioxidant and other processing.

Message

We will contact you within one working day. Please pay attention to your email.